牌号 Brand | 组成 Consist Of | 分子量 Average Molecular | 熔点 Tm (oC) | 玻璃化转变温度 Tg (oC) | 产品特点 Performance |
XCP-3000H | AA/HDO | 3000 | 55 | 缩短开放时间，降低熔融粘度，提高初始强度 shortens open time, lowers melt viscosity, increases initial strength
| |
FLP-3500H | 3500 | 55 | |||
XCP-R4500H | 4500 | 55 | |||
XCP-R8500HA | 8500 | 57 | |||
NOTP-3870-A3 | DDA/HDO | 3500 | 70 | ||
CTP-44 | AA/BDO | 2000 | 50 | 提高强度，降低使用温度范围 increases strength, lowers application temperature | |
XCP-TM3000B | 3000 | 55 | |||
FLP-2000N | AA/NPG | 2000 | -48 | 提高柔软度，提高耐溶剂性 increases flexibility, improves solvent resistance | |
PES-2000NB | AA/NPG/BDO | 2000 | -58 | 提高柔软度，提高耐水解性 increases flexibility, improves hydrolysis resistance | |
PES-2200NH | AA/NPG/HDO | 2000 | -60 | ||
CTP-244 | AA/EG/BDO | 2000 | -62 | ||
XCP-R2170 | - | 4000 | -15 | 延长开放时间，提高柔软度，降低熔融粘度，提高对非极性表面的粘结性 extends open time, increases flexibility, lowers melt viscosity, improves adhesion to non-polar (low energy) substrates | |
XCP-R2370 | - | 4000 | -30 | ||
XCP-R2570 | - | 5500 | -55 | ||
FLP-PA1000N | PA/NPG | 1000 | 26 | 提高熔融粘度，提高初始强度，提高对极性表面的粘结性 increases melt viscosity, increases initial strength, improves adhesion to polar substrates | |
XCP-R3170 | - | 3000 | 30 | ||
XCP-R5170 | - | 2600 | 50 | ||
XCPA-2000HL | PA/HDO | 2000 | -15 | 延长固化时间，降低熔融粘度，提高对非极性表面的粘结性 extends set time, lowers melt viscosity，improves adhesion to non-polar (low energy) substrates | |
XCP-2000IPS | - | 2000 | -22 | 提高耐水解性，提高耐温性 improves hydrolysis resistance, improves thermal stability |